EVA - Fast Curing EVA
Product explanation
- Surface: There are two kinds of surfaces of Fast Curing EVA - smooth plane surface and the rhombic surface.
- Thickness: All from 0.10mm to 0.80mm can be supplied, but EVA with 0.10-0.35mm thickness can only be provided with smooth plane surface, 0.40mm and the upper thickness can be supplied the above two different surfaces. 0.5mm thickness is normal product whose rhombic surface can reach 0.66 thickness.
- Width: We can supply any width within 1700mm and the general width is 280.350, 540, 670, 810, 820, 980, 1000mm etc.
- Length: Generally 100/150 meters per roll, or else as your requirement.
Technical data
| Properties |
Test Method |
Unit |
Fast Cure |
| F406 |
F806 |
| Density |
ISO 1183 |
g/cm³ |
0.96 |
0.96 |
| Tensile Stenght |
ISO 527-3 |
MPa |
16 |
16 |
| Elongation at break |
% |
550 |
550 |
| Young’s Modulus (cured) |
MPa |
4.7 |
4.7 |
| Hardness |
GB/T531-1999 |
Shore A |
72~75 |
72~75 |
| Optical Transmission (390-1105 nm) |
ASTM D1003 |
% |
>92.0 |
>92.0 |
| Refractive Index |
ISO 489 |
-- |
1.481 |
1.481 |
| UV-Cutoff Wavelength** |
UV-Vis` |
nm |
310 |
360 |
| UV Light resistance280nm~385nm, 15KWh/m² |
Q/HZF 001-2006 |
%TransmissionRetention |
>88 |
>90 |
| Heat/Humidity Resistance85ºC/85RH, 2000h |
|
>88 |
>88 |
| Cross-Linking Rate |
|
Gel % |
75-85 |
80-90 |
| Strength Peeling (Glass) |
|
N/cm |
>60 |
>60 |
| Strength Peeling (TPT) |
|
N/cm |
>40 |
>40 |
| Shrinkage Rate (120ºC, 3min) |
|
MD / TD % |
<4.0/<2.0 |
<4.0/<2.0 |
| Water-absorbing Rate |
GBT/T 1034-1998 |
% |
<0.1 |
<0.1 |
| Volume Insulating Resistance |
GBT/T 1410-2006 |
MΩ |
1.45x106 |
1.45x106 |
| Range of Thickness |
GBT/T 6672-2001 |
mm |
0.3 - 0.8 |
0.3 - 0.8 |
| Range of Width |
-- |
mm |
250-2,000 |
250-2,000 |
| Surface Finish |
-- |
-- |
Embossed (Single or Double Side) |
Fast Cure - One Step Method
| Lamination Condition |
F406 |
F807 |
| Hot Plate Temp (C) |
142 (140 - 148) |
145 (140 - 150) |
| Vacuum Time (min) |
5 - 7 |
3 - 5 |
| Press Time (min) |
12 - 15 |
8 - 12 | |
| |